Geocell

2023/4/28

Product performance

　　The sheet material of the geocell is made of linear polyethylene (PE) and polypropylene (PP), which are extruded and stretched after being heated at high temperatures. It has the ability to expand and contract freely, and can be transported and folded. During construction, it can be stretched into a mesh and filled with loose materials such as soil, crushed stone, and concrete, forming a structure with strong lateral limitations and high stiffness. Lightweight material, wear-resistant, chemically stable, resistant to light oxygen aging, acid and alkali, suitable for different soil conditions such as deserts.

Applicable scope

　　Soft foundation treatment of expressways, first-class highway, railways, municipal roads, airport roads and ports can also be used to control landslides, build retaining walls, bridge abutment jumping and landscaping.

Technical parameter

Reference standard GB/T19274-2003

Model	Cell height（H/mm）		Cell thickness（T/mm）	Cell welding distance（A/mm）
	Nominal value	deviation	Nominal value	Nominal value	deviation
1	H≤100	+1	≥1.1	330≤A＜800	+15
2	100＜H≤200	+2	≥1.1	330≤A＜800	+15

Serial Number	Test items	unit	Material PP compartment	Material PP compartment
1	appearance		The cells are flat, without bubbles or grooves
2	Longitudinal tensile yield strength of cells	Mpa	≥23	≥20
3	Tensile strength at the rivet	N/cm	≥100	≥100
4	Tensile strength at the connection between cell groups (cell edge)	N/cm	≥200	≥200
5	Tensile strength at the connection between cell groups (in the middle of the cell sheet)	N/cm	≥120	≥120

Reference standard Q/CR549.1-2016

Serial Number	project	index
1	tensile yield strength MPa	≥20
2	elongation at yield	≤15%
3	Right angle tear resistance N	≥120,The thickness of the cell is 0.8mm
3	Right angle tear resistance N	≥150，The thickness of the cell is 1.1mm
4	Environmental stress cracking time h	≥800
5	oxidation induction time min	≥20
6	carbon black dispersity	No more than 1 level 3 out of 10 data, and levels 4 and 5 are not allowed
7	Carbon black content	≥2.0%
8	Peel Strength N/cm	≥100
9	Tensile strength N/cm	≥190